Bridge Joint with Big Movement

• Customization: Available
• Connection: Welding
• Material: Carbon Steel
• Model NO.: D480
• Surface Treatment: Galvanized
• Customized: Customized
• Certification: CE, ISO9001
• Application: Steel
• Movement: 0-480mm
• Transport Package: as Request
• Specification: AASHTO
• Trademark: Haider
• Origin: China
• HS Code: 7308100000
• Production Capacity: 100, 000 Meters/Year

Product Description

Modular Expansion Joint, Bridge Expansion Joint

Modular Expansion Joint Systems have gained overwhelming worldwide acceptance for accommodating and sealing large joint movements on bridge structures. By incorporating the results of recent research activities, each joint system is designed to provide watertight, fatigue resistant, long-term, maintenance-free performance.

Design Principles

Fatigue Resistant
Modular expansion joint assemblies are subjected to millions of high dynamic stress cycles due to passing vehicle loads. Recognizing the significance of these dynamic loads on the long-term performance of expansion joint systems, Haider became the first China company to introduce fatigue-resistant design principles to modular expansion joint assemblies. It is strongly recommended that a specification which includes fatigue design provisions be included in the contract documents.

Watertight Integrity
Each Modular Expansion Joint System not only bridges the joint gap but also protects the structure from premature corrosion. Design of the strip seal sealing element is based on compression of the neoprene seal lug into the gland recess of the centerbeam and edge beam. This mechanically-locked neoprene seal not only provides excellent watertight characteristics but also achieves high pullout resistance.

 

Standard		JT/T4-2004		BS5400 Section 9.2
Rubber		Natural Rubber	Neoprene CR	Natural Rubber	Neoprene CR
Hardness(IRHD)		60±5	60±5	50±5/60±5/70±5
Tensile Strength (M Pa)≥		18	17	17	15.5
Ultimate Elongation (%)≥		450	400	450/400/350	400/350/300
Compression Set		70 o C×22h		70 o C×22h	100 o C×22h
		<30	<15	<30	<35
Heat Resistance	Test Condition	70 o C×168h	100 o C×70h	70 o C×168h	100 o C×48h
	Change in Hardness	-5,+10	0,+10	<10	<15
	(IRHD)
	Rate of Tensile Strength Reduction(%)	<15		<15
	Rate of Ultimate	<20	<40	<20	<40
	Elongation Reduction
	(%)
Ozone Resistance		25~50pphm,20% strain		25~50pphm,20% strain
		40 o C×96h		30 o C×96h
		No Cracks		No Cracks